The Constant Stress/Strain Flexometer measures the heating characteristics of a vulcanized rubber test piece when applied test amplitude the load (stress) controlling to a specified level applying to static load. It also performs tests by controlling a specified deflection (strain). Unlike conventional flexometers, this equipment adopts a special temperature detector to measure the inner temperature of a test piece during testing, thus making it possible to measure the real heat-up temperature. The tester can measure viscoelasticity parameters (such as E', E", and tanδ) simultaneously with a heat build-up test. There is also a fully automatic model that performs continued testing of up to 30 test pieces.
轮胎、橡胶输送带、橡胶滚子、防振橡胶等、在实际应用状态下反复受到大变形橡胶制品通过内部发热引起的耐疲劳性和振动吸收性能等，与制品试验关联性为0.99以上的划时代试验机能在实验室再现，诞生了领先21世纪要求的材料试验机。

技术参数：

试验片
形 状：圆柱状
尺 寸： （A） ø17.8×25ｍｍ 
        （B） ø30.0×25ｍｍ

静态负荷
负荷方法：液压缸、伺服控制
负 荷： 0～500Ｎ　连续可变（0～50kgf）

●Application Standard：JIS K 6265
●Test Frequency：5～50Hz
●Load：0～500N（Static Load）,0～1,500Np-p（Dynamic Load）
●Deflection：0～20mm（Static Deflection）,0～6.5mmp-p（Dynamic Deflection）
●Test Temperature：50～150℃

特长:
● 检出静态和动态的应变、应力，通过反馈伺服控制可以在高精度、稳定的条件下进行试验。
● 用伺服控制方法可自由地设定，以用过去的机器不可实现的定应力测定为主，各种各样的负荷方式、大范围的
   测定条件。
● 可进行与制品同样的负荷方式、条件下的模拟实验。
● 连续测定蠕变及大变形时的粘弹性基础数据。
● 从动态应变、应力波形直接实时测定、表示tan δ。
● 可以自动检验出爆裂（blow out），将发生时刻以仅仅n=1确切地决定。
● 开发时常能检验出试验片中心发热温度的新机构，大幅度地提高热作图（heat buid up）测定精度。
● 通过液压伺服驱动，可靠性强、机构非常简洁没有磨损或损坏部分，容易实现比原来更苛刻的测定条件。