产品描述
1) 中/英文软件
2) 加装DayLight滤镜可用于光伏材料光老化试验, 更换AM1.5滤镜后可用于光伏电池预衰减试验.
BR-UL-Xenon Ultraviolet Light Exposure Chamber
Implementation of standards:
① UL 1703-2008 Polymeric materials (quote UL 746C-2006“Ultraviolet Light Exposure”, spectral distribution conform to ASTM G155-2005)
② VDE 0126-5:2008 Junction box “Weather resistance test”, VDE 0126-3:2009 Connector “Weather resistance”，spectral distribution conform to ISO 4892-2-2006
③ ETAG 002-2000, ASTM C1184-2000 Silicone sealant UV age test, spectral distribution conform to ASTM G155-2005
④ General specification of crystalline silicon solar cell for terrestrial application: Cell maximum power in early light attenuation ratio test
| Effective area of irradiation: 500×400mm Measurement point or range: 300~400nm, 290~800nm, 340nm/nm, 420nm/nm Irradiation uniformity: better than ±10% at 312×312mm Irradiation deviation: ±2W/m2@300~400nm Temperature control range: RT~90°C±2.5°C Air temperature control range: 20~80°C With refrigeration compressor, spray system Irradiation, temperature and spray: Program control Irradiation and temperature closed loop control… |
| Wavelengh range | Transmission after filter | Benchmark solar | ASTM G155 | Radiation precent after filter |
| (<290nm) | 0.01% | 0~0.15% | 0~0.15% | 0.02% |
| (290~320nm) | 2.85% | 5.80% | 2.6~7.9% | 4.34% |
| (320~360nm) | 23.90% | 40.00% | 28.3~40.0% | 36.46% |
| (360~400nm) | 38.79% | 54.20% | 54.2~67.5% | 59.18% |
| Total UV | 65.54% | 100.00% | 100.00% | 100.00% |
| Physical-property consideration | Material test method |
| Functional support | Tensile strength or Flexural strength (The ultraviolet-exposed side is to be in contact with the two loading points when using the three-point loading method.) |
| Impact resistance | Tensile impact, Izod impact, or Charpy impact |