SAM-1550-2-2ps-x

1 week

 SAM: λ = 1550 nm, absorbance 2 %, Δ R = 1.2 %,
 relaxation time ~ 2ps

SAM-1550-4-2ps-x

1 week

 SAM: λ = 1550 nm, absorbance 4 %, Δ R = 2.4 %,
 relaxation time ~ 2ps

SAM-1550-6-2ps-x

1 week

 SAM: λ = 1550 nm, absorbance 6 %, Δ R = 3.6 %,
 relaxation time ~ 2ps

SAM-1550-7-5ps-x

1 week

 SAM: λ = 1550 nm, absorbance 7 %, Δ R = 4 %,
 relaxation time 5 ps

SAM-1550-8-2ps-x

1 week

 SAM: λ = 1550 nm, absorbance 8 %, Δ R = 5.5 %,
 relaxation time ~ 2ps

SAM-1550-10-2ps-x

1 week

 SAM: λ = 1550 nm, absorbance 10 %, Δ R = 6 %,
 relaxation time 2 ps

SAM-1550-10-5ps-x

1 week

 SAM: λ = 1550 nm, absorbance 10 %, Δ R = 6 %,
 relaxation time 5 ps

SAM-1550-12-2ps-x

1 week

 SAM: λ = 1550 nm, absorbance 12 %, Δ R = 7 %,
 relaxation time 2 ps

SAM-1550-12-5ps-x

1 week

 SAM: λ = 1550 nm, absorbance 12 %, Δ R = 7 %,
 relaxation time ~ 5 ps

SAM-1550-14-5ps-x

1 week

 SAM: λ = 1550 nm, absorbance 14 %, Δ R = 8 %,
 relaxation time 5 ps

SAM-1550-16-2ps-x

1 week

 SAM: λ = 1550 nm, absorbance 16 %, Δ R = 9 %,
 relaxation time ~ 2 ps

SAM-1550-17-2ps-x

1 week

 SAM: λ = 1550 nm, absorbance 17 %, Δ R = 10 %,
 relaxation time 2 ps

SAM-1550-17-4ps-x

1 week

 SAM: λ = 1550 nm, absorbance 17 %, Δ R = 10 %,
 relaxation time 4 ps

SAM-1550-20-4ps-x

1 week

 SAM: λ = 1550 nm, absorbance 20 %, Δ R = 12 %,
 relaxation time 4 ps

SAM-1550-21-2ps-x

1 week

 SAM: λ = 1550 nm, absorbance 21 %, Δ R = 13 %,
 relaxation time ~ 2 ps

SAM-1550-25-2ps-x

1 week

 SAM: λ = 1550 nm, absorbance 25 %, Δ R = 15 %,
 relaxation time 2 ps

SAM-1550-26-5ps-x

1 week

 SAM: λ = 1550 nm, absorbance 26 %, Δ R = 16 %,
 relaxation time 5 ps

SAM-1550-32-4ps-x

1 week

 SAM: λ = 1550 nm, absorbance 32 %, Δ R = 20 %,
 relaxation time 4 ps

SAM-1550-33-2ps-x

1 week

 SAM: λ = 1550 nm, absorbance 33 %, Δ R = 19 %,
 relaxation time 2 ps

SAM-1550-55-2ps-x

1 week

 SAM: λ = 1550 nm, absorbance 55 %, Δ R = 36 %,
 relaxation time ~ 2 ps

PHS

1 week

 passive heat sink for fiber coupled SAM