SAE ARP5144A-2017
热固性树脂固化的加热
Heat Application for Thermosetting Resin Curing
购买全文，请联系:
- 标准号
- SAE ARP5144A-2017
- 发布
- 2017年
- 发布单位
- SAE - SAE International
- 当前最新
- SAE ARP5144A-2017
- 适用范围
- This SAE Aerospace Recommended Practice (ARP) describes standard methods of heat application to cure thermosetting resins for commercial aircraft composite repairs. The methods described in this document shall only be used when specified in an approved repair document or with the agreement of the Original Equipment Manufacturer (OEM) or regulatory authority. Purpose The purpose of this document is to provide a number of standard heat application methods that may be referenced in repair documents produced by airlines or airframe and engine manufacturers. This document is one of several in support of other procedures required to perform composite repairs@ intended for use throughout the commercial aircraft industry. These include AIR4844@ AIR4938@ AIR5278@ ARP4916@ ARP4991 and others incorporated herein.
SAE ARP5144A-2017相似标准
推荐
塑料改性||热固性树脂特点、类型与用途
因此，热固性树脂的优点是耐热性高，受压不易变形。其缺点是机械性能较差。热固性树脂有酚醛、环氧、氨基、不饱和聚酯以及硅醚树脂等。热固性树脂作用机理在加热、加压下或在固化剂、紫外光作用下，进行化学反应，交联固化成为不溶不熔物质的一大类合成树脂。硬化后的塑料化学结构发生变化、质地坚硬、不溶于溶剂、加热也不再软化，如果温度过高则就分解或者碳化。...
里程碑的量热计术|Discovery X3 DSC在热固性材料中的最新应用
第二次加热测量重新固化后材料的 Tg，以及在固化温度下的任何的残余固化。实验双组分环氧树脂图 1 为双组分环氧树脂材料第一次加热的 DSC 数据。包装上说明该环氧树脂在 15 分钟后凝固，30 分钟后固化。...
专栏丨热塑性树脂VS热固性树脂：两者相较，各有千秋
近年来，也出现一些热塑性树脂与连续纤维共用形成创新结构复合物产品的实例，相比于热固性塑料，热塑塑料尽管有一些明显的优点，然而许多缺陷却也不容忽视。不过，热固性树脂一旦交联固化成型，无法可逆，不能再次成型。因此，热固性树脂是一次性材料，难以回收再利用。然而，目前有数家新型企业表示，已经通过高温热解反应成功实现了废弃树脂材料的降解，并完成强化纤维的回收。目前，热固性塑料和热塑性塑料的生产技术日益进步。...
塑料成型工艺动图合集，让你看过瘾！
成型经过加热使其熔化，加压冲模，再经过加热交联固化，脱模后既得制品。主要用于热固性树脂的成型。14．树脂传递模塑成型是将树脂注入到闭合模具中浸润增强材料并固化的工艺方法。该项技术可不用预浸料、热压罐，有效地降低设备成本、成型成本。该项技术近年来发展很快，在飞机工业、汽车工业、舰船工业等领域应用日广，并研究发展出RFI 、VARTM 、SCRIMP 、SPRINT等多种分支，满足不同领域的应用需求。...