ASTM A276/A276M-23
不锈钢棒材和型材标准规范
Standard Specification for Stainless Steel Bars and Shapes
ASTM A276/A276M-23 发布历史
ASTM A276/A276M-23由美国材料与试验协会 US-ASTM 发布于 2023-08-01。
ASTM A276/A276M-23在国际标准分类中归属于: 77.140.20 不锈钢。
ASTM A276/A276M-23 不锈钢棒材和型材标准规范的最新版本是哪一版？
最新版本是 ASTM A276/A276M-24a 。
ASTM A276/A276M-23 发布之时，引用了标准
- ASTM A1058 钢制品机械试验的标准试验方法&x2014公制*， 2024-06-23 更新
- ASTM A314 锻造用不锈及耐热钢坯及钢棒的标准规范
- ASTM A370 钢铁产品机械试验的标准试验方法和定义
- ASTM A484/A484M 不锈钢棒材、坯料、型材和锻件的一般要求标准规范*， 2024-01-01 更新
- ASTM A582/A582M 自由加工不锈钢棒标准规范
- ASTM A751 钢铁产品化学分析的标准测试方法 实践和术语
- ASTM E527 金属和合金编号的标准实施规程（UNS）
- SAE J1086 金属和合金编号
* 在 ASTM A276/A276M-23 发布之后有更新，请注意新发布标准的变化。
ASTM A276/A276M-23的历代版本如下：
- 2024年 ASTM A276/A276M-24a 不锈钢棒材和型材标准规范
- 2024年 ASTM A276/A276M-24 不锈钢棒材和型材标准规范
- 2023年 ASTM A276/A276M-23 不锈钢棒材和型材标准规范
- 2017年 ASTM A276/A276M-17 不锈钢棒和形状的标准规格
- 2016年 ASTM A276/A276M-16a 不锈钢棒材和型材的标准规格
- 2016年 ASTM A276/A276M-16 不锈钢棒材和型材的标准规格
- 2015年 ASTM A276/A276M-15 不锈钢棒材和型材的标准规格
- 2013年 ASTM A276-13a 不锈钢棒材和型材标准规格
- 2013年 ASTM A276-13 不锈钢棒材和型材的标准规格
- 2010年 ASTM A276-10 不锈钢钢筋和型材的标准规范
- 2008年 ASTM A276-08a 不锈钢棒和形状的标准规格
- 2008年 ASTM A276-08 不锈钢棒和形状的标准规格
- 2006年 ASTM A276-06 不锈钢钢棒和型材的标准规范
- 2005年 ASTM A276-05a 不锈钢棒材和型材的标准规范
- 2005年 ASTM A276-05 不锈钢棒材和型材的标准规范
- 2004年 ASTM A276-04 不锈钢棒材和型材标准规范
- 2003年 ASTM A276-03 不锈钢棒的标准规范
- 2002年 ASTM A276-02a 不锈钢棒材和型材标准规范
- 2002年 ASTM A276-02 不锈钢棒材和型材标准规范
- 2000年 ASTM A276-00ae1 不锈钢棒材和型材标准规范
- 2000年 ASTM A276-00a 不锈钢棒材和型材标准规范
- 1998年 ASTM A276-98b 不锈钢棒和形状的标准规格
1.1 This specification covers hot-finished or cold-finished bars except bars for reforging (Note 1). It includes rounds, squares, and hexagons, and hot-rolled or extruded shapes, such as angles, tees, and channels in the more commonly used types of stainless steels. The free-machining types (Note 2) for general corrosion resistance and high-temperature service are covered in a separate specification. NOTE 1—For bars for reforging, see Specification A314. NOTE 2—For free-machining stainless bars designed especially for optimum machinability, see Specification A582/A582M. NOTE 3—There are standards covering high nickel, chromium, austenitic corrosion, and heat-resisting alloy materials. These standards are under the jurisdiction of ASTM Subcommittee B02.07 and may be found in Annual Book of ASTM Standards, Vol. 02.04. 1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. The inch-pound units shall apply unless the “M” designation of this specification is specified in the order. 1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
- 标准号
- ASTM A276/A276M-23
- 发布
- 2023年
- 发布单位
- 美国材料与试验协会
- 替代标准
- ASTM A276/A276M-24
- 当前最新
- ASTM A276/A276M-24a
- 引用标准
- ASTM A1058 ASTM A314 ASTM A370 ASTM A484/A484M ASTM A582/A582M ASTM A751 ASTM E527 SAE J1086
ASTM A276/A276M-23相似标准
推荐
棒材拉力试验机介绍
钢材有线材、板材、型材和棒材，这些钢材轧制出来的形状不用用途也不一样，棒材就是截面是园的，粗细在20mm以上的钢材。棒材一般指的是棒料，是指产品断面形状为圆形、方形、扁形、棒材用途六角形、八角形等简单断面，并以直条交货的钢材（混凝土用钢筋除外），属于高碳钢，硬度比较大，一般用作机加工。...
无损检测的磁粉检测相关介绍
适用性和局限性： 磁粉探伤适用于检测铁磁性材料表面和近表面尺寸很小、间隙极窄（如可检测出长0.1mm、宽为微米级的裂纹）目视难以看出的不连续性；也可对原材料、半成品、成品工件和在役的零部件检测，还可对板材、型材、管材、棒材、焊接件、铸钢件及锻钢件进行检测，可发现裂纹、夹杂、发纹、白点、折叠、冷隔和疏松等缺陷。 ...
大、小规格结构钢低倍组织评级图间的差异及联系
1 评级图的制作GB/T1979-1980《结构钢低倍组织缺陷评级图》在执行20年来，对保证和提高我国钢铁产品的质量起到了巨大的作用，尤其是特钢企业的不锈钢、碳素钢、纯铁、合金结构钢的轧材、锻材、钢坯等均参照本标准进行内部试验及出厂产品的检验。...
何为磁粉探伤
b.磁粉检测可对原材料、半成品、成品工件和在役的零部件检测，还可对板材、型材、管材、棒材、焊接件、铸钢件及锻钢件进行检测。c.可发现裂纹、夹杂、发纹、白点、折叠、冷隔和疏松等缺陷。d.磁粉检测不能检测奥氏体不锈钢材料和用奥氏体不锈钢焊条焊接的焊缝，也不能检测铜、铝、镁、钛等非磁性材料。对于表面浅的划伤、埋藏较深的孔洞和与工件表面夹角小于20°的分层和折叠难以发现。...