AMS5622A-1984

Steel Bars@ Forgings@ Tubing@ and Rings@ Corrosion Resistant 16Cr - 4.0Ni - 0.30(Cb + Ta) - 4.0Cu Solution Heat Treated@ Consumable Electrode Melted Precipitation Hardenable (UNS S17400)

AMS5622A-1984 发布历史

Form: This specification covers a premium aircraft-quality corrosion- ~ resistant steel in the form of bars@ wire@ forgings@ mechanical tubing@ flash welded rings@ and stock for forging@ flash welded rings@ or heading. Application: Primarily for parts requiring corrosion resistance and high strength up to 600??(315??. Certain processing procedures and service conditions may cause these products to become subject to stress-corrosion cracking; ARP 1110 recommends practices to minimize such conditions. For applications@ such as bolting@ where stress-corrosion is a possibility@ the product should be precipitation heat treated for not less ( than 4 hr at the highest temperature compatible with the strength requirements but in no case lower than 1025??(550??. Classification: Product covered by this specification is classified as S1 follows: Type I - Steel multiple melted using vacuum consumable electrode in the final melt. Type II - Steel multiple melted using electroslag process in the final melting. Unless a specific type is ordered@ either type may be supplied.

AMS5622A-1984由SAE - SAE International 发布于 1984-04-01，并于 2011-01-28 实施。

AMS5622A-1984的历代版本如下：

• 1984年04月01日 AMS5622A-1984

非常抱歉，我们暂时无法提供预览，您可以试试： 免费下载 AMS5622A-1984 前三页，或者稍后再访问。

注意： 点击下载后，生成下载文件时间比较长，请耐心等待......

标准号

AMS5622A-1984

发布日期

1984年04月01日

实施日期

2011年01月28日

废止日期

无

中国标准分类号

/

国际标准分类号

/

发布单位

SAE - SAE International

引用标准

11

适用范围

Form: This specification covers a premium aircraft-quality corrosion- ~ resistant steel in the form of bars@ wire@ forgings@ mechanical tubing@ flash welded rings@ and stock for forging@ flash welded rings@ or heading. Application: Primarily for parts requiring corrosion resistance and high strength up to 600??(315??. Certain processing procedures and service conditions may cause these products to become subject to stress-corrosion cracking; ARP 1110 recommends practices to minimize such conditions. For applications@ such as bolting@ where stress-corrosion is a possibility@ the product should be precipitation heat treated for not less ( than 4 hr at the highest temperature compatible with the strength requirements but in no case lower than 1025??(550??. Classification: Product covered by this specification is classified as S1 follows: Type I - Steel multiple melted using vacuum consumable electrode in the final melt. Type II - Steel multiple melted using electroslag process in the final melting. Unless a specific type is ordered@ either type may be supplied.