GSO ISO 23529:2008由GSO 发布于 2008-09-03。
GSO ISO 23529:2008在国际标准分类中归属于: 83.060 橡胶。
GSO ISO 23529:2008 橡胶 物理试验方法中制备和调节试样的一般方法的最新版本是哪一版?
最新版本是 GSO ISO 23529:2008 。
This International Standard specifies general procedures for the preparation, measurement, marking, storage and conditioning of rubber test pieces for use in physical tests specified in other International Standards, and the preferred conditions to be used during the tests. Special conditions applicable to a particular test or material or simulating a particular climatic environment are not included, nor are special requirements for testing whole products. This International Standard also specifies the requirements for the time-interval to be observed between forming and testing of rubber test pieces and products. Such requirements are necessary to obtain reproducible test results and to minimize disagreements between customer and supplier.
举例说明一下,如果你是做橡胶制品的拉力测试,根据《硫化橡胶和热塑性橡胶拉伸性能的测定》GB/T528-2001标准和GB9865硫化橡胶样品和试样的制备标准规定,橡胶试样一般宽度6mm,厚度2mm即截面积12m㎡,橡胶试样的强度一般为5—20Mpa,所以橡胶试样的拉力一般为50—500N,如遇特殊试样可视情况而定,橡胶制品的微电脑拉力试验机的量程一般选择500N—2500N。...
皮革物理和机械试验耐磨性能的测定 主要用于检测各种具有耐磨性能要求的皮革。TABER耐磨试验机引用标准:GB250评定变色用灰色样卡QB/T2706皮革、化学、物理、机械和色牢度试样取样部位QB/T2707皮革 物理和机械试验 试样的准备各调节TABER耐磨试验机试验原理:被测试的试样放在水平平台上旋转,两个磨轮被赋予特定的压力压在试片上旋转。...
2.粘合效果不稳定 有时因粘合不牢使试样在磨耗过程中开裂,导致试验失败。 3.部分试样粘合困难 一般胶轮由通用橡胶制成,与硅橡胶和氟橡胶等特种橡胶粘合较为困难。 4.粘合接头处理复杂 接头粘合一般采用双斜角接头方法,试验常常因接头处破坏而失败。 ...
塑料拉力机橡胶拉力机,拉伸,拉力机,行程,夹具>塑料和橡胶的拉伸性能是其力学性能中重要、基本的性能之一,它在很大程度上决定了该种塑料和橡胶的使用场合。拉伸性能的好坏,可以通过拉伸试验来检测。塑料拉力机橡胶拉力机的拉伸性能作为材料使用时要求高分子聚合物具有的力学性能。可以说,对于高分子聚合物的大部分应用而言,力学性能比其他物理性能显得更为重要。...