SAE ARP 4715-2000
钢部件的感应淬火

Induction Hardening of Steel Components

SAE ARP 4715-2000 发布历史

This recommended practice provides guidelines for the establishment of an induction hardening process for steel components. It is intended to be used as a guide for designers of induction hardened parts, for process auditors, and for purchase specifications and/or process sheets as applicable. Induction heat treatment is intended for hardening of only selected areas of plain carbon or alloy steel components. A prior heat treatment may be specified for improved response of the overall component to induction hardening, or for control of properties in the balance of the part. AMS 2759 is recommended for such prior heat treatment.

SAE ARP 4715-2000由美国机动车工程师协会 US-SAE 发布于 2000。

SAE ARP 4715-2000 在中国标准分类中归属于: V11 航空与航天用金属铸锻材料，在国际标准分类中归属于: 49.025.05 黑色金属合金综合。

SAE ARP 4715-2000 发布之时，引用了标准

• SAE J 423-1998 测量表面硬化深度方法
• SAE AMS 2649B-1996 高强度钢部件腐蚀检验
• SAE AMS 2759C-2000 钢部件热处理的一般要求
• SAE ARP 1820A-1997 

SAE ARP 4715-2000的历代版本如下：

• 2000年 SAE ARP 4715-2000 钢部件的感应淬火

非常抱歉，我们暂时无法提供预览，您可以试试： 免费下载 SAE ARP 4715-2000 前三页，或者稍后再访问。

注意： 点击下载后，生成下载文件时间比较长，请耐心等待......

标准号

SAE ARP 4715-2000

发布日期

2000年

实施日期

废止日期

无

中国标准分类号

V11

国际标准分类号

49.025.05

发布单位

US-SAE

引用标准

ASTM E 18-2000 ASTM E 92-1982 ASTM E 112-1996 ASTM E 384-1999 SAE J 423-1998 SAE AMS 2649 SAE AMS 2649B-1996 SAE AMS 2759 SAE AMS 2759C-2000 SAE ARP 1820-1984 SAE ARP 1820A-1997

适用范围

This recommended practice provides guidelines for the establishment of an induction hardening process for steel components. It is intended to be used as a guide for designers of induction hardened parts, for process auditors, and for purchase specifications and/or process sheets as applicable. Induction heat treatment is intended for hardening of only selected areas of plain carbon or alloy steel components. A prior heat treatment may be specified for improved response of the overall component to induction hardening, or for control of properties in the balance of the part. AMS 2759 is recommended for such prior heat treatment.