BS ISO 1268-3-2000
纤维增强塑料.试验板的制备方法.湿压缩模塑法

Fibre-reinforced plastics - Methods of producing test plates - Wet compression moulding

BS ISO 1268-3-2000 发布历史

This part of ISO 1268 specifies a method of making test plates by wet compression moulding. Using this method, test plates can be made in a reproducible manner, making it possible to compare the results of tests carried out at differ-ent times and/or in different places. Test specimens cut from plates made by wet compression moulding are useful in characterizing the reinforcement used. The reinforcement can be either mats or fabrics. The following properties of these materials are of particular interest: — water absorption (ISO 62); — flexural strength and flexural modulus (ISO 178); — impact strength (Charpy) (ISO 179); — tensile strength, tensile modulus and elongation at break (ISO 527-4). This part of ISO 1268 is intended to be used in conjunction with ISO 1268-1.

BS ISO 1268-3-2000由英国标准学会 GB-BSI 发布于 2001-03-15，并于 2001-03-15 实施。

BS ISO 1268-3-2000 在中国标准分类中归属于: Q23 纤维增强复合材料，在国际标准分类中归属于: 83.120 增强塑料,83.140.10 薄膜和薄板。

BS ISO 1268-3-2000的历代版本如下：

• 2001年03月15日 BS ISO 1268-3-2000 纤维增强塑料.试验板的制备方法.湿压缩模塑法
• 2001年03月15日 BS ISO 1268-3-2001 纤维增强塑料.试验板的制备方法.湿压缩模塑法

非常抱歉，我们暂时无法提供预览，您可以试试： 免费下载 BS ISO 1268-3-2000 前三页，或者稍后再访问。

注意： 点击下载后，生成下载文件时间比较长，请耐心等待......

标准号

BS ISO 1268-3-2000

发布日期

2001年03月15日

实施日期

2001年03月15日

废止日期

无

中国标准分类号

Q23

国际标准分类号

83.120;83.140.10

发布单位

GB-BSI

被代替标准

98/121103 DC-1998 BS 2782-9 Methods 920A to 920C-1977

适用范围

This part of ISO 1268 specifies a method of making test plates by wet compression moulding. Using this method, test plates can be made in a reproducible manner, making it possible to compare the results of tests carried out at differ-ent times and/or in different places. Test specimens cut from plates made by wet compression moulding are useful in characterizing the reinforcement used. The reinforcement can be either mats or fabrics. The following properties of these materials are of particular interest: — water absorption (ISO 62); — flexural strength and flexural modulus (ISO 178); — impact strength (Charpy) (ISO 179); — tensile strength, tensile modulus and elongation at break (ISO 527-4). This part of ISO 1268 is intended to be used in conjunction with ISO 1268-1.