DIN EN ISO 13807-2009
釉瓷和搪瓷 化学工业用瓷层热冲击试验中裂纹形成温度的测定

Vitreous and porcelain enamels - Determination of crack formation temperature in the thermal shock testing of enamels for the chemical industry (ISO 13807:1999, including Cor 1:2000); English version of DIN EN ISO 13807:2009-04

DIN EN ISO 13807-2009 发布历史

This International Standard specifies a test method for the determination of the crack formation temperature of enamels for the chemical industry by subjecting enamelled steel specimens to thermal shock using cold water. The value of the crack formation temperature measured according to this test method is not valid for the finished component (see annex A). It is a parameter of vitreous and porcelain enamels for comparing the relative quality of different enamel formulations.

DIN EN ISO 13807-2009由德国标准化学会 DE-DIN 发布于 2009-04。

DIN EN ISO 13807-2009 在中国标准分类中归属于: Y26 日用搪瓷制品。

DIN EN ISO 13807-2009 发布之时，引用了标准

• ISO 2808 ISO 2808-2019
• ISO 3819 实验室玻璃器皿.烧杯*， 2015-12-01 更新
• ISO 2746 釉瓷和搪瓷.高电压试验*， 2015-10-01 更新

* 在 DIN EN ISO 13807-2009 发布之后有更新，请注意新发布标准的变化。

DIN EN ISO 13807-2009的历代版本如下：

• 2009年04月 DIN EN ISO 13807-2009 釉瓷和搪瓷 化学工业用瓷层热冲击试验中裂纹形成温度的测定

非常抱歉，我们暂时无法提供预览，您可以试试： 免费下载 DIN EN ISO 13807-2009 前三页，或者稍后再访问。

注意： 点击下载后，生成下载文件时间比较长，请耐心等待......

标准号

DIN EN ISO 13807-2009

发布日期

2009年04月

实施日期

废止日期

无

中国标准分类号

Y26

国际标准分类号

25.220.50

发布单位

DE-DIN

引用标准

ISO 2808 ISO 3819 ISO 10141 ISO 2746

被代替标准

DIN ISO 13807-2001 DIN EN ISO 13807-2008

适用范围

This International Standard specifies a test method for the determination of the crack formation temperature of enamels for the chemical industry by subjecting enamelled steel specimens to thermal shock using cold water. The value of the crack formation temperature measured according to this test method is not valid for the finished component (see annex A). It is a parameter of vitreous and porcelain enamels for comparing the relative quality of different enamel formulations.

谁引用了DIN EN ISO 13807-2009 更多引用