1.1 General This International Standard specifies four methods for the determination of the hardness of vulcanized or thermoplastic rubbers on flat surfaces (standard-hardness methods) and four methods for the determination of the apparent hardness of curved surfaces (apparent-hardness methods). The hardness is expressed in international rubber hardness degrees (IRHD). The methods cover the hardness range from 10 IRHD to 100 IRHD. The methods differ primarily in the diameter of the indenting ball and the magnitude of the indenting force, these being chosen to suit the particular application. The range of applicability of each method is indicated in Figure 1. The determination of hardness by a pocket hardness meter is described in ISO 7619-2. 1.2 Standard-hardness methods Method N: Normal test -- This method is appropriate for rubbers with a hardness in the range 35 IRHD to 85 IRHD, but may also be used for hardnesses in the range 30 IRHD to 95 IRHD. Method H: High-hardness test -- This method is appropriate for rubbers with a hardness in the range 85 IRHD to 100 IRHD. Method L: Low-hardness test -- This method is appropriate for rubbers with a hardness in the range 10 IRHD to 35 IRHD. Method M: Microtest -- This method is essentially a scaled-down version of the normal test method N, permitting the testing of thinner and smaller test pieces. It is appropriate for rubbers with a hardness in the range 35 IRHD to 85 IRHD, but may also be used for hardnesses in the range 30 IRHD to 95 IRHD NOTE 1 The value of the hardness obtained by method N within the ranges from 85 IRHD to 95 IRHD and from 30 IRHD to 35 IRHD may not agree precisely with that obtained using method H or method L, respectively. The difference is not normally significant for technical purposes. NOTE 2 Because of various surface effects in the rubber and the possibility of slight surface roughness (produced, for example, by buffing), the microtest may not always give results agreeing with those obtained by the normal test. 1.3 Apparent-hardness methods Also specified are four methods. CN CH. CL and CM, for the determination of the apparent hardness of curved surfaces. These methods are modifications of methods N, H, L and M. respectively, for cases where the rubber surface tested is curved. Two cases exist, depending whether a) the test piece or product tested is large enough for the hardness instrument to rest upon it; b) it is small enough for both the test piece and the instrument to rest upon a common support. A variant of b) would be where the test piece rests on the specimen table of the instrument Apparent hardness can also be measured an non-standard flat test pieces usJng methods N, H, L and M. The procedures described cannot provide for all possible shapes and dimensions of test piece, but cover some of the commonest types, such as O-rings Determination of the apparent hardness of rubber-covered rollers is dealt with separately in the various parts of ISO 7267
DIN ISO 48-2009由德国标准化学会 DE-DIN 发布于 2009-10。
DIN ISO 48-2009 在中国标准分类中归属于: G35 合成橡胶,在国际标准分类中归属于: 83.060 橡胶。
* 在 DIN ISO 48-2009 发布之后有更新,请注意新发布标准的变化。
非常抱歉,我们暂时无法提供预览,您可以试试: 免费下载 DIN ISO 48-2009 前三页,或者稍后再访问。
点击下载后,生成下载文件时间比较长,请耐心等待......
Copyright ©2007-2022 ANTPEDIA, All Rights Reserved
京ICP备07018254号 京公网安备1101085018 电信与信息服务业务经营许可证:京ICP证110310号