SAE AMS 6472E-2010
112 ksi(772 MPa)抗拉强度、渗氮法1.6Cr 0.35Mo 1.1Al(0.38-0.43C)(135 Mod)淬火和回火的钢棒和钢铸件

Steel Bars and Forgings, Nitriding 1.6Cr 0.35Mo 1.1Al (0.38-0.43C)(135 Mod) Hardened and Tempered, 112 ksi (772 MPa) Tensile Strength

SAE AMS 6472E-2010 发布历史

This specification covers an aircraft-quality, low-alloy steel in the form of heat treated bars and forgings, and of forging stock. This material has been used typically for nitrided parts requiring high surface hardness, resistance to heat, and less distortion than parts made from steel requiring quenching to case harden. This steel may be case hardened in dissociated ammonia gas to give a minimum case hardness of 900 HV.

SAE AMS 6472E-2010由美国机动车工程师协会 US-SAE 发布于 2010-05-17。

SAE AMS 6472E-2010 在中国标准分类中归属于: V11 航空与航天用金属铸锻材料，在国际标准分类中归属于: 49.025.10 钢。

SAE AMS 6472E-2010的历代版本如下：

• 2010年05月17日 SAE AMS 6472E-2010 112 ksi(772 MPa)抗拉强度、渗氮法1.6Cr 0.35Mo 1.1Al(0.38-0.43C)(135 Mod)淬火和回火的钢棒和钢铸件

SAE AMS 6472E-2010 112 ksi(772 MPa)抗拉强度、渗氮法1.6Cr 0.35Mo 1.1Al(0.38-0.43C)(135 Mod)淬火和回火的钢棒和钢铸件 于 2014-07-29 变更为 SAE AMS 6472F-2014 112 ksi(772 MPa)抗拉强度、渗氮法1.6Cr-0.35Mo-1.1Al(0.38-0.43C)(135 Mod)淬火和回火的钢棒和钢铸件。

非常抱歉，我们暂时无法提供预览，您可以试试： 免费下载 SAE AMS 6472E-2010 前三页，或者稍后再访问。

注意： 点击下载后，生成下载文件时间比较长，请耐心等待......

标准号

SAE AMS 6472E-2010

发布日期

2010年05月17日

实施日期

废止日期

无

中国标准分类号

V11

国际标准分类号

49.025.10

发布单位

US-SAE

代替标准

SAE AMS 6472F-2014

适用范围

This specification covers an aircraft-quality, low-alloy steel in the form of heat treated bars and forgings, and of forging stock. This material has been used typically for nitrided parts requiring high surface hardness, resistance to heat, and less distortion than parts made from steel requiring quenching to case harden. This steel may be case hardened in dissociated ammonia gas to give a minimum case hardness of 900 HV.