SAE AMS2580-2010由美国机动车工程师协会 US-SAE 发布于 2010-05-17。
SAE AMS2580-2010 在中国标准分类中归属于: V18 冷加工工艺,在国际标准分类中归属于: 49.040 有关航空航天制造用镀涂和有关工艺。
This specification covers the requirements for inducing compressive residual stresses on the surface of metal parts using ultrasonically activated shot peening. Ultrasonically activated shot peening is typically used to induce compressive residual stresses on the surface layer of metallic parts to a depth up to 0.040 inch (1 mm). The shape and depth of the compressive residual stress distribution depend on the properties of the part and the ultrasonically activated shot peening process parameters. The residual stresses produced increase fatigue performance, resistance to stress-corrosion cracking, corrosion fatigue, and fretting fatigue, but its usage is not limited to such applications.
喷丸强化是一种受控喷丸技术,不同于喷丸清理。喷丸清理以去除工件表面油污、氧化皮、锈蚀和机械加工毛刺为目的。齿轮表面的喷丸强化主要是借助于高速运动的弹丸冲击零件的表面,使其发生弹性塑性变形,从而产生残余压应力、加工硬化和组织细化等有利的变化,以提高齿轮的弯曲疲劳强度和接触疲劳强度,是改善齿轮抗咬合能力、提高齿轮使用寿命的重要途径。...
冷加工引起的塑性变形会导致残余应力的产生。残余应力的程度和性质(拉应力或压应力)取决于加工过程的程度和类型。喷丸强化是一种冷加工工艺,在该工艺中,零件表面用称为喷丸的小球进行喷丸处理。该过程会在零件表面引起塑性变形,减少零件表面拉应力并引入有益的残余压应力。喷丸强化是类似于表面滚压的过程,两者都是表面塑性变形以形成残余压应力的深度分布。...
喷砂喷丸粗糙度仪的大小,对机械零件的使用性能有很大的影响。在加工过程,使用粗糙度仪测量零件的粗糙度非常重要。 ...