SAE AMS 5518M-2014
拉伸强度为150ksi(1034 MPa)18Cr-8Ni冷轧钢制耐腐蚀薄板材和带材

Steel, Corrosion Resistant, Sheet and Strip 18Cr - 8Ni Cold Rolled, 150 Ksi (1034 MPa) Tensile Strength

SAE AMS 5518M-2014 发布历史

This specification covers a corrosion-resistant steel in the form of sheet and strip. These products have been used typically for parts requiring strength and moderate forming or bending, but usage is not limited to such applications. Mechanical properties specified herein are obtained by cold working (strain hardening) and not by heat treatment. Therefore, the cold-worked product should not be heated to a temperature which adversely affects the mechanical properties or corrosion resistance before, during, or after fabrication.

SAE AMS 5518M-2014由美国机动车工程师协会 US-SAE 发布于 2014-06-12。

SAE AMS 5518M-2014 在中国标准分类中归属于: H40 钢铁产品综合，在国际标准分类中归属于: 49.025.10 钢。

SAE AMS 5518M-2014 发布之时，引用了标准

• ASTM A370-2013 钢制品机械测试的标准试验方法和定义*， 2022-07-27 更新
• ASTM E290-2013 测定材料延展性的弯曲试验的标准试验方法*， 2022-07-27 更新
• ASTM E384-2011 材料努氏和维氏硬度的标准试验方法*， 2022-07-27 更新
• AMS2371 
• AMS2807 

* 在 SAE AMS 5518M-2014 发布之后有更新，请注意新发布标准的变化。

SAE AMS 5518M-2014的历代版本如下：

• 2014年06月12日 SAE AMS 5518M-2014 拉伸强度为150ksi(1034 MPa)18Cr-8Ni冷轧钢制耐腐蚀薄板材和带材

SAE AMS 5518M-2014 由 SAE AMS 5518L-2008 变更而来。

非常抱歉，我们暂时无法提供预览，您可以试试： 免费下载 SAE AMS 5518M-2014 前三页，或者稍后再访问。

注意： 点击下载后，生成下载文件时间比较长，请耐心等待......

标准号

SAE AMS 5518M-2014

发布日期

2014年06月12日

实施日期

废止日期

无

中国标准分类号

H40

国际标准分类号

49.025.10

发布单位

US-SAE

引用标准

ASTM A370-2013 ASTM E290-2013 ASTM E353-1993 ASTM E384-2011 SAE AMS 2242 AMS2248 AMS2371 AMS2807

被代替标准

SAE AMS 5518L-2008

适用范围

This specification covers a corrosion-resistant steel in the form of sheet and strip. These products have been used typically for parts requiring strength and moderate forming or bending, but usage is not limited to such applications. Mechanical properties specified herein are obtained by cold working (strain hardening) and not by heat treatment. Therefore, the cold-worked product should not be heated to a temperature which adversely affects the mechanical properties or corrosion resistance before, during, or after fabrication.