5.1 Fracture toughness is expressed in terms of an elastic-plastic stress intensity factor, KJc, that is derived from the J-integral calculated at fracture.
5.2 Ferritic steels are microscopically inhomogeneous with respect to the orientation of individual grains. Also, grain boundaries have properties distinct from those of the grains. Both contain carbides or nonmetallic inclusions that can act as nucleation sites for cleavage microcracks. The random location of such nucleation sites with respect to the position of the crack front manifests itself as variability of the associated fracture toughness (16). This results in a distribution of fracture toughness values that is amenable to characterization using the statistical methods in this test method.
5.3 The statistical methods in this test method presume that the test materials are macroscopically homogeneous such that both the tensile and toughness properties are uniform. The fracture toughness evaluation of nonuniform materials is not amenable to the statistical analysis methods employed in the main body of this test method. For example, multipass weldments can create heat-affected and brittle zones with localized properties that are quite different from either the bulk material or weld. Thick section steel also often exhibits some variation in properties near the surfaces. An appendix to analyze the cleavage toughness properties of nonuniform or inhomogeneous materials is currently being prepared. In the interim, users are referred to (6-8) for procedures to analyze inhomogeneous materials. Metallographic analysis can be used to identify possible nonuniform regions in a material. These regions can then be evaluated through mechanical testing such as hardness, microhardness, and tensile testing to compare with the bulk material. It is also advisable to measure the toughness properties of these nonuniform regions distinctly from the bulk material.
5.4 Distributions of KJc data from replicate tests can be used to predict distributions of KJc for different specimen sizes. Theoretical reasoning (12), confirmed by experimental data, suggests that a fixed Weibull slope of 4 applies to all data distributions and, as a consequence, standard deviation on data scatter can be calculated. Data distribution and specimen size effects are characterized using a Weibull function that is coupled with weakest-link statistics (17). An upper limit on constraint loss and a lower limit on test temperature are defined between which weakest-link statistics can be used.
5.5 The experimental results can be used to define a master curve that describes......
-01 断裂韧性测定的标准试验方法 Standard Test Method for Measurement of Fracture Toughness E1823-96(2002) 疲劳和裂纹试验相关的标准术语 Standard Terminology Relating to Fatigue and Fracture Testing E1921-05 测定铁素体钢在转变范围内基准温度的标准试验方法...
落锤式冲击试验机主要用于测定铁素体钢(包括板材、型材、铸钢和锻钢)的无塑性转变温度。无塑性转变温度表征含有小裂纹的钢材在动态加载屈服应力下发生脆断的zui高温度。试验方法是将一定质量的锤体提升到一定高度,然后由静止释放,锤体自由落体冲击到试样表面,从而给试样进行动态加载。该试验机集机、电、自动控制技术于一体,实现了送料、提锤、冲击、出样、抓锤的全自动化过程。...
研究人员提出了一种校准多相场模型参数的方法,即模拟TRIP钢中奥氏体分解为铁素体和贝氏体,在奥氏体晶界处引入铁素体形核中心,用合适的界面迁移率,解释实验中铁素体的形成的动力学机制;贝氏体成核是在合适的界面位置(即奥氏体晶界,奥氏体-铁素体界面),或在很高的过冷度下的奥氏体晶粒内发生。...
图1. 1Cr17钢加热到900℃后空冷的组织为铁素体+沿轧制方向分布碳化物 图2. 1Cr17钢淬火后组织为铁素体+低碳马氏体1.2 马氏体不锈钢基体为马氏体组织,有磁性,通过热处理可调整其力学性能的不锈钢。马氏体不锈钢在高温状态的组织为奥氏体,经过淬火后,奥氏体转变为马氏体,故称其为马氏体不锈钢。...
Copyright ©2007-2022 ANTPEDIA, All Rights Reserved
京ICP备07018254号 京公网安备1101085018 电信与信息服务业务经营许可证:京ICP证110310号