ASTM E1245-03(2016)
通过自动图像分析测定金属内含物或者第二相组分含量的标准实施规程

Standard Practice for Determining the Inclusion or Second-Phase Constituent Content of Metals by Automatic Image Analysis

被代替

标准号

ASTM E1245-03(2016)

发布

2003年

发布单位

美国材料与试验协会

替代标准

ASTM E1245-03(2023)

当前最新

ASTM E1245-03(2023)

 

 

引用标准

ASTM E3 ASTM E45 ASTM E7 ASTM E768

适用范围

5.1 This practice is used to assess the indigenous inclusions or second-phase constituents of metals using basic stereological procedures performed by automatic image analyzers.

5.2 This practice is not suitable for assessing the exogenous inclusions in steels and other metals. Because of the sporadic, unpredictable nature of the distribution of exogenous inclusions, other methods involving complete inspection, for example, ultrasonics, must be used to locate their presence. The exact nature of the exogenous material can then be determined by sectioning into the suspect region followed by serial, step-wise grinding to expose the exogenous matter for identification and individual measurement. Direct size measurement rather than application of stereological methods is employed.

5.3 Because the characteristics of the indigenous inclusion population vary within a given lot of material due to the influence of compositional fluctuations, solidification conditions and processing, the lot must be sampled statistically to assess its inclusion content. The largest lot sampled is the heat lot but smaller lots, for example, the product of an ingot, within the heat may be sampled as a separate lot. The sampling of a given lot must be adequate for the lot size and characteristics.

5.4 The practice is suitable for assessment of the indigenous inclusions in any steel (or other metal) product regardless of its size or shape as long as enough different fields can be measured to obtain reasonable statistical confidence in the data. Because the specifics of the manufacture of the product do influence the morphological characteristics of the inclusions, the report should state the relevant manufacturing details, that is, data regarding the deformation history of the product.

5.5 To compare the inclusion measurement results from different lots of the same or similar types of steels, or other metals, a standard sampling scheme should be adopted such as described in Practice E45.

5.6 The test measurement procedures are based on the statistically exact mathematical relationships of stereology4 for planar surfaces through a three-dimensional object examined using reflected light (see Note 1).

5.7 The orientation of the sectioning plane relative to the hot-working axis of the product will influence test results. In general, a longitudinally oriented test specimen surface is employed in order to assess the degree of elongation of the malleable (that is, deformable) inclusions.

5.8 Oxide inclusion measurements for cast metals, or for wrought sections that are not fully consolidated, may be biased by partial or complete detection of fine porosity or microshrinkage cavities and are not recommended. Sulfides can be discriminated from such voids in most instances and such measurements may be performed.

5.9 Results of such measurements may be used to qualify material for shipment according to a......

全自动仪器—送给您的劳动节礼物

食用油中极性组分（PC）检测“黄金拍档”　　《GB 5009.202-2016 食品安全国家标准 食用油中极性组分（PC）的测定》于2017年3月1日实施，其中第一法为制备型快速柱层析法，博纳艾杰尔推出的 EOPC全自动食用油极性组分分离系统同步国标方法，适用于食用油中的极性组分含量测定。　　Cleanert EOPC 食用油极性组分专用柱替代手工装填的层析柱，保证测试结果准确、可靠 。...

xps和eds的区别

e) 一些很难见到的稀土元素或者La系Ac系元素，这很可能是因为噪音的峰较强，仪器的分析认为有微量相应能量区的元素存在，用软件去除即可。　　XRD （X射线物相定性分析）　　用X射线衍射数据对样品中存在的物相（而不是化学成分中的元素构成）进行鉴别。测定结晶情况，晶相，晶体结构及成键状态等等；可以确定各种晶态组分的结构和含量。　　...

EDS,XRD,XPS有什么不同

e) 一些很难见到的稀土元素或者La系Ac系元素，这很可能是因为噪音的峰较强，仪器的分析认为有微量相应能量区的元素存在，用软件去除即可。　　XRD （X射线物相定性分析）　　用X射线衍射数据对样品中存在的物相（而不是化学成分中的元素构成）进行鉴别。测定结晶情况，晶相，晶体结构及成键状态等等；可以确定各种晶态组分的结构和含量。　　...

2019-2021：爆发的气相自动进样器市场（上）

三级冷阱预浓缩基本原理和过程是：气体样品以一定的流速从采样罐中泵到系统中， 首先在第一级冷阱中通过液氮（或者干冰）制冷将气态的水变成固态的冰，从而实现样品和水的分离；其次，在第二级冷阱使待测化合物与二氧化碳及其他空气中主要成分分离；然后，将待测组分聚焦在第三级冷阱中进行进一步浓缩；最后，引入气相色谱仪器/气质联用仪器中进行分离和分析。　　...